奥氏体标号表.doc_咨信网zixin.com.cn

资源描述

一.奥氏体，马氏体，沉淀硬化型不锈钢的化学成分表类型钢号牌号化学成分 %　　　　　　　　　　 C Cr Ni Mn P S Mo Si Cu N 其它奥氏体型 201 1Cr17Mn6Ni5N ≤0.15 16.00-18.00 3.50-5.50 5.50－7.50 ≤0.060 ≤0.030 - ≤1.00 - ≤0.25 - 201L 03Cr17Mn6Ni5N ≤0.030 16.00-18.00 3.50-5.50 5.50－7.50 ≤0.060 ≤0.030 　 ≤1.00 　 ≤0.25 　 202 1Cr18Mn8Ni5N ≤0.15 17.00-19.00 4.00-6.00 7.50-10.00 ≤0.060 ≤0.030 　 ≤1.00 - ≤0.25 － 204 03Cr16Mn8Ni2N ≤0.030 15.00-17.00 1.50-3.50 7.00-9.00 　　　　　 0.15-0.30 　国内研制 1Cr18Mn10Ni5Mo3N ≤0.10 17.00-19.00 4.00-6.00 8.50-12.00 　　 2.80-3.50 　　 0.20-0.30 　前苏联 2Cr13Mn9Ni4 0.15-0.25 12.00-14.00 3.70-5.00 8.00-10.00 　　　　　　　国内研制 2Cr15Mn15Ni2N 0.15-0.25 14.00-16.00 1.50-3.00 14.00-16.00 　　　　　 0.15-0.30 　　 1Cr18Mn10Ni5Mo3N ≤0.15 17.00-19.00 4.00-6.00 8.50-12.00 ≤0.060 ≤0.030 2.8-3.5 ≤1.00 - 0.20-0.30 - 301 1Cr17Ni7 ≤0.15 16.00-18.00 6.00-8.00 ≤2.00 ≤0.065 ≤0.030 - ≤1.00 - - - 302 1Cr18Ni9 ≤0.15 17.00-19.00 8.00-10.00 ≤2.00 ≤0.035 ≤0.030 - ≤1.00 - - - 303 Y1Cr18Ni9 ≤0.15 17.00-19.00 8.00-10.00 ≤2.00 ≤0.20 ≤0.030 1) ≤1.00 - - - 303se Y1Cr18Ni9Se ≤0.15 17.00-19.00 8.00-10.00 ≤2.00 ≤0.20 ≤0.030 - ≤1.00 - - Se≥0.15 304 0Cr18Ni9 ≤0.07 17.00-19.00 8.00-10.00 ≤2.00 ≤0.035 ≤0.030 - ≤1.00 - - - 304L 00Cr19Ni10 ≤0.030 18.00-20.00 8.00-10.00 ≤2.00 ≤0.035 ≤0.030 - ≤1.00 - - - 304N1 0Cr19Ni9N ≤0.08 18.00-20.00 7.00-10.50 ≤2.00 ≤0.035 ≤0.030 - ≤1.00 - 0.10-0.25 - 304N2 0Cr18Ni10NbN ≤0.08 18.00-20.00 7.50-10.50 ≤2.00 ≤0.035 ≤0.030 - ≤1.00 - 0.15-0.30 Nb≤0.15 304LN 00Cr18Ni10N ≤0.030 17.00-19.00 8.50-11.50 ≤2.00 ≤0.035 ≤0.030 - ≤1.00 - 0.12-0.22 - 305 1Cr18Ni12 ≤0.12 17.00-19.00 10.50-13.00 ≤2.00 ≤0.035 ≤0.030 - ≤1.00 - - - 309S 0Cr23Ni13 ≤0.08 22.00-24.00 12.00-15.00 ≤2.00 ≤0.035 ≤0.030 - ≤1.00 - - - 310S 0Cr25Ni20 ≤0.08 24.00-26.00 19.00-22.00 ≤2.00 ≤0.035 ≤0.030 - ≤1.00 - - - 316 0Cr17Ni12Mo2 ≤0.08 16.00-18.50 10.00-14.00 ≤2.00 ≤0.035 ≤0.030 2.00-3.00 ≤1.00 - - - 　 1Cr18Ni12Mo2Ti6) ≤0.12 16.00-19.00 11.00-14.00 ≤2.00 ≤0.035 ≤0.030 1.80-2.50 ≤1.00 - - Ti5(C%-0.02)~0.08 　 0Cr18Ni12Mo2Ti ≤0.08 16.00-19.00 11.00-14.00 ≤2.00 ≤0.035 ≤0.030 1.80-2.50 ≤1.00 - - Ti5*C%-0.70 316L 00Cr17Ni14Mo2 ≤0.030 16.00-18.00 12.00-15.00 ≤2.00 ≤0.035 ≤0.030 2.00-3.00 ≤1.00 - - - 316N 0Cr17Ni12Mo2N ≤0.08 16.00-18.00 10.00-14.00 ≤2.00 ≤0.035 ≤0.030 2.00-3.00 ≤1.00 - 0.10-0.22 - 316N 00Cr17Ni13Mo2N ≤0.030 16.00-18.50 10.50-14.50 ≤2.00 ≤0.035 ≤0.030 2.00-3.00 ≤1.00 - 0.12-0.22 - 316J1 0Cr18Ni12Mo2Cu2 ≤0.08 17.00-19.00 10.00-14.50 ≤2.00 ≤0.035 ≤0.030 1.20-2.75 ≤1.00 1.00-2.50 - - 316J1L 00Cr18Ni14Mo2Cu2 ≤0.030 17.00-19.00 12.00-16.00 ≤2.00 ≤0.035 ≤0.030 1.20-2.75 ≤1.00 1.00-2.50 - - 317 0Cr19Ni13Mo3 ≤0.12 18.00-20.00 11.00-15.00 ≤2.00 ≤0.035 ≤0.030 3.00-4.00 ≤1.00 - - - 317L 00Cr19Ni13Mo3 ≤0.08 18.00-20.00 11.00-15.00 ≤2.00 ≤0.035 ≤0.030 3.00-4.00 ≤1.00 - - - 　 1Cr18Ni12Mo3Ti6) ≤0.12 16.00-19.00 11.00-14.00 ≤2.00 ≤0.035 ≤0.030 2.50-3.50 ≤1.00 - - Ti5(C%-0.02)~0.08 　 0Cr18Ni12Mo3Ti ≤0.08 16.00-19.00 11.00-14.00 ≤2.00 ≤0.035 ≤0.030 2.50-3.50 ≤1.00 - - Ti5*C%-0.70 317J1 0Cr18Ni16Mo5 ≤0.040 16.00-19.00 15.00-17.00 ≤2.00 ≤0.035 ≤0.030 4.00-6.00 ≤1.00 - - - 321 1Cr18Ni9Ti6) ≤0.12 17.00-19.00 8.00-11.00 ≤2.00 ≤0.035 ≤0.030 - ≤1.00 - - Ti5(C%-0.02)~0.08 　 0Cr18Ni10Ti ≤0.08 17.00-19.00 9.00-12.00 ≤2.00 ≤0.035 ≤0.030 - ≤1.00 - - Ti≥5*C% 347 0Cr18Ni11Nb ≤0.08 17.00-19.00 9.00-13.00 ≤2.00 ≤0.035 ≤0.030 - ≤1.00 - - Nb≥10*C% XM7 0Cr18Ni9Cu3 ≤0.08 17.00-19.00 8.50-10.50 ≤2.00 ≤0.035 ≤0.030 - ≤1.00 3.00-4.00 - - XM15J1 0Cr18Ni13Si4 ≤0.08 15.00-20.00 11.50-15.00 ≤2.00 ≤0.035 ≤0.030 - 3.00-5.00 - - 2) 奥氏体 | 铁素体 329J1 0Cr26Ni5Mo2 ≤0.08 23.00-28.00 3.00-6.00 ≤1.50 ≤0.035 ≤0.030 1.00-3.00 ≤1.00 - - 2) 　 1Cr18Ni11Si4AlTi 0.10-0.18 17.50-19.50 10.--120.. ≤0.80 ≤0.035 ≤0.030 - 3.40-4.00 - - Al 0.10-0.30; Ti 0.40-0.70 　 00Cr18Ni5MoSi2 ≤0.030 18.00-19.50 4.50-5.50 1.00-2.00 ≤0.035 ≤0.030 2.50-3.00 1.30-2.00 - - - 铁素体型 405 0Cr13Al ≤0.08 11.50-14.50 3) ≤1.00 ≤0.035 ≤0.030 - ≤1.00 - - Al 0.10-0.30 410L 00Cr12 ≤0.030 11.00-13.00 3) ≤1.00 ≤0.035 ≤0.030 - ≤1.00 - - - 430 1Cr17 ≤0.12 16.00-18.00 3) ≤1.25 ≤0.035 ≤0.030 - ≤0.75 - - - 430F Y1Cr17 ≤0.12 16.00-18.00 3) ≤1.00 ≤0.035 ≥0.15 1) ≤1.00 - - - 434 1Cr17Mo ≤0.12 16.00-18.00 3) ≤1.00 ≤0.035 ≤0.030 0.75-1.25 ≤1.00 - - - 447J1 00Cr30Mo2 ≤0.010 28.50-32.00 - ≤0.40 ≤0.035 ≤0.030 1.50-2.50 ≤0.40 - ≤0.015 - XM27 00Cr27Mo ≤0.010 25.00-27.50 - ≤0.40 ≤0.035 ≤0.030 0.75-1.50 ≤0.40 - ≤0.015 - 马氏体型 403 1Cr12 ≤0.15 11.50-13.00 3) ≤1.00 ≤0.035 ≤0.030 - ≤0.50 - - - 410 1Cr13 ≤0.15 11.50-13.50 3) ≤1.00 ≤0.035 ≤0.030 - ≤1.00 - - - 405 0Cr13 ≤0.08 11.50-13.50 3) ≤1.00 ≤0.035 ≤0.030 - ≤1.00 - - - 416 Y1Cr13 ≤0.15 12.00-14.00 3) ≤1.25 ≤0.035 ≥0.15 1) ≤1.00 - - - 410J1 1Cr13Mo ≤0.08-0.18 11.50-14.00 3) ≤1.00 ≤0.035 ≤0.030 0.30-0.60 ≤0.60 - - - 420J1 2Cr13 0.16-0.25 12.00-14.00 3) ≤1.00 ≤0.035 ≤0.030 - ≤1.00 - - - 420J2 3Cr13 0.26-0.35 12.00-14.00 3) ≤1.00 ≤0.035 ≤0.030 - ≤1.00 - - - 420F Y3Cr13 0.26-0.40 12.00-14.00 3) ≤1.25 ≤0.035 ≥0.15 1) ≤1.00 - - - 　 3Cr13Mo 0.28-0.35 12.00-14.00 3) ≤1.00 ≤0.035 ≤0.030 0.50-1.00 ≤0.80 - - - 　 4Cr13 0.36-0.45 12.00-14.00 3) ≤0.80 ≤0.035 ≤0.030 - ≤0.60 - - - 431 1Cr17Ni2 0.11-0.17 16.00-18.00 1.50-2.50 ≤0.80 ≤0.035 ≤0.030 - ≤0.80 - - - 440A 7Cr17 0.60-0.75 16.00-18.00 3) ≤1.00 ≤0.035 ≤0.030 4) ≤1.00 - - - 440B 8Cr17 0.75-0.95 16.00-18.00 3) ≤1.00 ≤0.035 ≤0.030 4) ≤1.00 - - - 　 9Cr18 0.90-1.00 17.00-19.00 3) ≤0.80 ≤0.035 ≤0.030 4) ≤0.80 - - - 440C 11Cr17 0.95-1.20 16.00-18.00 3) ≤1.00 ≤0.035 ≤0.030 4) ≤1.00 - - - 440F Y11Cr17 0.95-1.20 16.00-18.00 3) ≤1.25 ≤0.035 ≥0.15 4) ≤1.00 - - - 　 9Cr18Mo 0.95-1.10 16.00-18.00 3) ≤0.80 ≤0.035 ≤0.030 0.40-0.70 ≤0.80 - - - 　 9Cr18MoV 0.85-0.95 17.00-19.00 3) ≤0.80 ≤0.035 ≤0.030 1.00-1.30 ≤0.80 - - V0.07-0.12 沉淀硬化型 630 0Cr17Ni4Cu4Nb ≤0.07 15.50-17.50 6.50-7.50 ≤1.00 ≤0.035 ≤0.030 - ≤1.00 3.00-5.00 - Nb 0.15-0.45 631 0Cr17Ni7Al ≤0.09 16.00-18.00 6.50-7.50 ≤1.00 ≤0.035 ≤0.030 - ≤1.00 ≤0.50 - Al 0.75-1.50 632 0Cr15Ni7Mo2Al ≤0.09 14.00-16.00 6.50-7.50 ≤1.00 ≤0.035 ≤0.030 2.00-3.00 ≤1.00 - - Al 0.75-1.50

展开阅读全文