专业英语词汇の粉末冶金英语.doc

粉末冶金材料术语中英对照版
与材料有关的术语
烧结工艺
烧结材料 sintered material
预烧 presintering
烧结铁 sintered iron
连续烧结 continuous sintering
烧结钢 sintered steel
间歇烧结 batch sintering
重合金 heavy metal
活化烧结 activated sintering
弥散强化材料 dispersion－strengthened material
加压烧结 pressure sintering
金属陶瓷 cermet
气压烧结 gas pressure
烧结金属基复合材料 sintered metal－matrix composite MMC
松装粉末烧结 loose－powder sintering
与应用有关的术语
反应烧结 reaction sintering
烧结零件 sintered part
液相烧结 liquid－sintering
烧结结构零件 sintered structural part
固相烧结 solid－sintering
含油轴承 oil-retaining bearing
过烧 oversintering
烧结金属过滤器 sintered metal filter
欠烧 undersintering
烧结磁性零件 sintered magnetic part
熔渗 infiltration
烧结摩擦材料 sintered friction material
粘结剂脱除 binder removal
烧结电触头材料 sintered electrical contact material
脱蜡 dewaxing，burn－off
烧结后处理
快速烧除 rapid burn－off
复压 re-pressing
碳化 carburizing
精整 sizing
烧结 sintering
整形 coining
填料 packing material
粉末锻造 powder forging
吸气剂 getter
烧结锻造 sinter forging
造孔剂 pore－forming material
热复压 hot re-pressing
粘结相 binder phase
浸渍 impregnation
粘结金属 binder metal
水蒸气处理 steam treatment
压坯性能
烧结零件性能
生坯 green
密度 density
生坯密度 green density
相对密度 relative density
生坯强度 green strength
实体密度 solid density
棱边强度 edge strength
密度分布 density distribution
中立层 neutral zone
径向压溃强度 radial crushing strength
压制裂纹 pressing crack
孔隙 pore
分层 lamination
开孔 open pore
弹性后效 spring back
闭孔 closed pore
模具和接合器
空隙度 porosity
模具 mould
开孔空隙度 open porosity
模架 tool set
闭孔空隙度 closed porosity
接合器 adaptor
连通孔隙 interconnected porosity
接合器台板 adaptor table
扩散孔隙 diffusing porosity
阴模 die
孔隙结构 porosity structure
阴模固定板 die plate
孔径 pore size
楔铁 wedge
孔径分布 pore size distribution
上模冲 upper punch
起泡压力 bubble－point pressure
模冲固定板 punch plate
含油量 oil content
底板 base plate，lower coupler plate
流体透过性 fluid permeability
下模冲 lower punch
表观硬度 apparent hardness
模套 bolster
实体硬度 solid hardness
压紧环 clamp ring
网状氧化物 oxide network
柱 column
表层指状氧化物 surface finger oxide
芯棒 core rod
烧结现象
拨叉 fork
烧结颈形成 neck formation
调节杆 lifting rod
起泡 blistering
装粉靴 feed shoe
发汗 sweating
上压头 upper ram
胀大 growth
下压头 lower ram
收缩 shrinkage
模冲 punch
烧结壳 sinter skin
组合模冲segmented punch
烧结条件和烧结炉
脱模器 ejector
烧结温度 sintering temperature
多模具接合器 multiple－tool adaptor
烧结时间 sintering sintered time
倒锥 back relief
烧结气氛 sintering atmosphere
多工件模架 multiple－die set
烧结炉 sintering furnace
浮动阴模 floating die
真空炉 vacuum furnace
可拆阴模 split die
连续炉 continuous furnace
复合阴模 sandwich die
间歇炉 batch furnace
拼合阴模 segmenged die
网带炉mesh belt furnace
成形条件
步进梁式炉 walking－beam furnace
装粉量 fill
推杆式炉 pusher furnace
容积装粉法 volume filling
粉末性能，测试方法，测试设备和测试结果
重量装粉法 weight filling
自然坡角度 angle of repose
振动装粉法 vibration－assisted filling
松装密度 apparent density
过量装粉法 overfill system
散装密度 bulk density
欠量装粉法 underfill system
振实密度 tap density
装粉位置 fill position
压缩性 compressibility
装粉高度 fill height
成形性 compactibility
装粉体积 fill volume
压缩比 compression ratio
压制压力 compacting pressure
装填系数 fill factor
保压时间 dwell time
流动性 flowability
脱模操作 ejection process
流动时间 flow time
拉下脱模法 withdrawal process
氢损 hydrogen loss
拉下位置 withdrawal position
氢可还原氧 hydrogen－reducible oxygen
平衡压力 counrer－pressure
离析 demixing，segregation
上模冲压紧压力 top－punch hold－down pressure
比表面积 specific surface area
粉末冶金压制工艺
分级 classification
冷压 cold pressing
粒度 particle size
温压 warm pressing
粒度分布 particle size distribution
热压 hot pressing
淘析 elutriation
单轴向压制 uniaxial pressing
粒度级 cut
单向压制 single－actio pressing
筛分析 sieve analysis，screen analysis，screen classification
双向压制 double－action pressing
沉降 sedimentation
多模压制 multiple pressing
取样器 sample thief
等静压制 isostatic pressing
分样器 sample splitter
冷等静压制 cold isostatic pressing
套筛 sieve set
温袋等静压制 wet－bag isostatic pressing
流速计 flowmeter
干袋等静压制 dry－bag isostatic pressing
振实密度仪 tapping appparatus
热等静压制 hot isostatic pressing
筛上物 oversize
装套 encapsulation
筛下物 undersize
封装 canning
细粉 fines
金属粉末注射成形 metal injection moulding
筛上颗粒 oversize particle
粉末轧制 powder rolling
筛下颗粒 undersize particle
振动压制 vibration－assisted compaction
拱桥效应 bridfing
连续喷雾沉积 continuous－spray deposition
成形 forming
修形 shaping
固结 consolidation
增塑粉末挤压 plasticized－powder extrusion
压制 pressing
粉末
压制成形 compacting
粉末 powder
压坯 compact，green compact
颗粒 particle
毛坯 blank
团粒 agglomerate
复合压坯 compound compact
粉浆 slurry
预成形坯 perform
粉块 cake
骨架 skeleton
坯料 feedstock
粉末颗粒形状
粉末类型
颗粒形状 particle shape
雾化粉 atomized powder
针状 acicular
羰基粉 carbonyl powder
角状 angular
粉碎粉 comminuted powder
树枝状 dendritic
电解粉 electrolytic powder
纤维状 fibrous
沉淀粉 precopitated powder
片状 flaky，flaked
还原粉 reduced powder
粒状 granular
海绵粉 sponge powder
不规则状 irregular
合金粉 alloyed powder
瘤状 nodular
完全合金粉 completely alloyed powder
球状 spheroidal
预合金粉 pre－alloyed powder
粉末预处理
部分合金化粉 patically alloyed powder
合批 blending
扩散合金粉 diffusion alloyed powder
混合 mixing
机械合金化粉 mechanically alloyed powder
研磨 milling
母合金粉 master alloyed powder
制粒 granulation
复合粉 composite powder
喷雾干燥 spray drying
包裹粉 coated powder
超生雾化 ultrasonic gas－atomizing
合批粉 blended powder
快速冷凝 chill－block cooling
混合粉 mixed powder
反应研磨 reaction milling
预混合粉 pre－mixed powder
机械合金化 mechanical alloying
氢化－脱氢粉 dehydride powder
其它
快速冷凝粉 rapidly solidfied powder
磨削 grinding
捣碎粉 chopped powder
铣削 milling
超声震荡气化雾化粉 ultrasonically gas－atomized powder
裂变 fission

摩擦 friction
粉末添加剂
机器 machine 仪器 instrument 设备 equipment
粘结剂 binder
加工面/作业面 functional surface
掺杂剂 dopant
临近表面 adjacent surface
润滑剂 lubricant
缺口 nick
增塑剂 plasticizer
刻痕，槽口 notch
增溶剂 solubilizer
裂纹，瑕疵 flaws
防锈剂 rust preventive
刮痕 scatch
清洗剂 cleaning agent
气泡 blow hole
光亮剂 lustre-coating agent
锐边 sharp edge
金相 metallography
毛刺 burr 去毛刺 burr removal / deburr

倒圆角 round

扩孔器，铰刀，铰孔 reamer
回火马氏体tempered martensite
粗加工 rough machining
网状碳化物carbide network
淬火harden 回火temper
电阻炉electric resistance furnace

保温时间 soaking time

粉末冶金名词解释
1、烧结sintering
粉末或压坯在低于主要组分熔点的温度下的热处理，目的在于通过颗粒间的冶金结合以提高其强度。
2、填料packing material
在预烧或烧结过程中为了起分隔和保护作用而将压坯埋入其中的一种材料。
3、预烧pre-sintering
在低于最终烧结温度的温度下对压坯的加热处理。
4、加压烧结pressure
在烧结同时施加单轴向压力的烧结工艺。
5、松装烧结loose-powder sintering，gravity sintering
粉末未经压制直接进行的烧结。
6、液相烧结liquid-phase sintering
至少具有两种组分的粉末或压坯在形成一种液相的状态下烧结。
7、过烧over sintering
烧结温度过高和（或）烧结时间过长致使产品最终性能恶化的烧结。
8、欠烧under sintering
烧结温度过低和（或）烧结时间过短致使产品未达到所需性能的烧结。
9、熔渗infiltration
用熔点比制品熔点低的金属或合金在熔融状态下充填未烧结的或烧结的制品内的孔隙的工艺方法。
10、脱蜡dewaxing，burn-off
用加热排出压坯中的有机添加剂（粘结剂或润滑剂）。
11、网带炉meshbelt furnace
一般由马弗保护的网带将零件实现炉内连续输送的烧结炉。
12、步进梁式炉walking-beam furnace
通过步进梁系统将放置于烧结盘中的零件在炉内进行传送的烧结炉。
13、推杆式炉pusher furnace
将零件装入烧舟中，通过推进系统将零件在炉内进行传送的烧结炉。
14、烧结颈形成neck formation
烧结时在颗粒间形成颈状的联结。
15、起泡blistering
由于气体剧烈排出，在烧结件表面形成鼓泡的现象。
16、发汗sweating
压坯加热处理时液相渗出的现象。
17、烧结壳sinter skin
烧结时，烧结件上形成的一种表面层，其性能不同于产品内部。
18、相对密度relative density
多孔体的密度与无孔状态下同一成分材料的密度之比，以百分率表示。
19、径向压溃密度radial crushing strength
通过施加径向压力测定的烧结圆筒试样的破裂强度。
20、孔隙度porosity
多孔体中所有孔隙的体积与总体积之比。
21、扩散孔隙diffusion porosity
由于柯肯达尔效应导致的一种组元物质扩散到另一组元中形成的孔隙。
22、孔径分布poresize distribution
材料中存在的各级孔径按数量或体积计算的百分率。
23、表观硬度apparent hardness
在规定条件下测定的烧结材料的硬度，它包括了孔隙的影响。
24、实体硬度solid hardness
在规定条件下测定的烧结材料的某一相或颗粒或某一区域的硬度，它排除了孔隙的影响。
25、起泡压力bubble-point pressure
迫使气体通过液体浸渍的制品产生第一气泡所需的最小的压力。
26、流体透过性fluid permeability
在规定条件下测定的在单位时间内液体或气体通过多孔体的数量。