阀门材料化学成份表.xls

阀门主体材料的化学成份及机械性能表化学成份（%）残留元素机械性能钢种钢号CMnPSSiCuNiWCrMoV总量抗拉强度/Mpa屈服强度/Mpa延伸率/%断面收缩率/%-29425WCB0.30b1.0b0.040 0.045 0.60 0.300.500.500.200.031.00 485655 2502235-29425WCC0.25c1.20c0.040 0.045 0.60 0.300.500.500.200.031.00 485655 2752235595WC60.050.200.500.80 0.040 0.045 0.60 0.500.500.101.00 1.01.50 0.450.65485655 2752035600WC90.050.180.400.70 0.040 0.045 0.60 0.500.500.101.002.002.75 0.901.2485655 2752035C50.200.400.70 0.040 0.045 0.75 0.500.500.101.00 4.06.5 0.450.65620795 4151835CF80.081.500.040 0.04 2.008.011.018.021.04852053535CF8M0.081.500.040 0.04 1.509.012.018.021.04852053030CF30.031.500.040 0.04 1.508.012.017.021.04852053535CF3M0.031.500.040 0.04 1.509.013.017.021.04852053030LCB0.301.000.040 0.045 0.60 0.300.500.500.200.031.00 450650 2402435LCC0.251.200.040 0.045 0.60 0.300.500.500.200.031.00 485655 2752235Fe-18Cr-8NiCF80.081.500.040 0.04 2.008.011.018.021.03040.082.000.045 0.03 1.008.010.518.021.0Fe-18Cr-9Ni-2MoCF8M0.081.500.040 0.04 2.009.012.018.021.0 2.03.03160.082.000.045 0.03 1.0010.014.016.018.0 2.03.0注:b规定的最高含碳量每减少0.01%，允许最高含锰量增加0.04%，直到其最大含量达1.28%。C规定的最高含碳量每减少0.01%，允许最高含锰量增加0.04%，直到其最大含量达1.4%。冲击性能 夏比V型缺口(焦耳)两个和三个试样最少平均值单个试样最少值试验温度/1814-462016-46b规定的最高含碳量每减少0.01%，允许最高含锰量增加0.04%，直到其最大含量达1.28%。C规定的最高含碳量每减少0.01%，允许最高含锰量增加0.04%，直到其最大含量达1.4%。含碳量在最大规定值下减少0.01%，允许最高含锰量增加0.04%，直到其最大含量(LCB)达到1.28%,LCC到1.40%含碳量在最大规定值下减少0.01%，允许最高含锰量增加0.04%，直到其最大含量(LCB)达到1.28%,LCC到1.40%