常用铝合金特性对比演示课件.ppt

Click to edit Master title style,Click to edit Master text styles,Second level,Third level,Fourth level,Fifth level,*,*,常用铝合金特性对比,1,铝合金的典型机械性能,(Typical Mechanical Properties),铝合金牌号,及状态,拉伸强度,(MPa),屈服强度,(MPa),硬度力球,延伸率,(1/16in),厚度,5052-H112,175,195,60,12,5083-H112,180,211,65,14,6061-T651,310,276,95,12,7050-T7451,510,455,135,10,7075-T651,572,503,150,11,2024-T351,470,325,120,20,铝合金的典型物理性能,(Typical Physical Properties),铝合金牌号及状态,热膨胀系数,(20)m/mk,熔点范围,(,),电导率,()(%IACS),电阻率,()mm2/m,密度,()(g/cm3),2024-T351,23.2,500-635,30,0.058,2.82,5052-H112,23.8,607-650,35,0.050,2.72,5083-H112,23.4,570-640,29,0.059,2.72,6061-T651,23.6,580-650,43,0.040,2.73,7050-T7451,23.5,490-630,41,0.0415,2.82,7075-T651,23.6,475-635,33,0.0515,2.82,2,铝合金的化学成份,(Chemical Composition Limit Of Aluminum),合金,牌号,硅,Si,铁,Fe,铜,Cu,锰,Mn,镁,Mg,铬,Cr,锌,Zn,钛,Ti,其它,铝,每个,合计,最小值,2024,23.2,0.5,3.8-4.9,0.3-0.9,1.2-1.8,0.1,0.25,0.15,0.05,0.15,余量,5052,25,0.4,0.1,0.1,2.2-2.8,0.15-0.35,0.1,-,0.05,0.15,余量,5083,23.8,0.4,0.1,0.3-1.0,4.0-4.9,0.05-0.25,0.25,0.15,0.05,0.15,余量,6061,23.6,0.7,0.15-0.4,0.15,0.8-1.2,0.04-0.35,0.25,0.15,0.05,0.15,余量,7050,23.5,0.15,20.-2.6,0.1,1.9-2.6,0.04,5.7-6.7,0.06,0.05,0.15,余量,7075,23.6,0.5,1.2-2.0,0.3,2.1-2.9,0.18-0.28,5.1-6.1,0.2,0.05,0.15,余量,3,美铝典型应用领域,用 途,2024,5052,5083,6061,7050,7075,农业,-,-,-,-,航空器,-,-,模具,-,-,-,机械设备,-,五金零件,-,-,-,-,-,建筑,-,-,-,-,机动车,-,-,-,-,建筑产品,-,-,-,-,化学设备,-,-,-,-,-,集装箱,-,-,-,-,-,-,烹饪用具,-,-,-,-,-,-,圆筒或活塞,-,-,-,-,泵体,-,-,-,-,-,电子,-,-,-,-,-,电工,-,-,-,-,紧固件,-,屏蔽线,-,-,-,-,-,风叶,-,-,-,-,-,家具,-,-,-,-,-,筒状容器,-,-,-,-,-,-,硬件装置,-,-,医疗设备,-,-,-,-,厨房设备,-,-,-,-,灯座,-,-,-,-,-,-,水上用途,-,-,-,-,机械配件,-,-,名称招牌,-,-,-,-,-,-,军火用品,-,-,管道,-,-,-,-,-,车体,-,-,-,-,娱乐设施,-,-,储存箱,-,-,-,-,架构,-,-,-,-,-,卡车与拖车,-,-,-,-,拉链,-,-,-,-,-,-,4,2A12,铝合金为一种高强度硬铝,不能进行热处理强化,。,2A12,铝合金点焊焊接性良好，用气焊和氩弧焊时有形成晶间裂纹的倾向；,2A12,铝合金在冷作硬化后可切削性能尚好。抗蚀性不高,常采用阳极氧化处理与涂漆方法或表面加包铝层以提高抗腐蚀能力。用途主要用于制作各种高负荷的零件和构件（但不包括冲压件锻件）如飞机上的骨架零件，蒙皮，隔框，翼肋，翼梁，铆钉等,150,以下工作零件。,化学成分,(Chemical Composition Limits wt%),分析：,合金牌号,旧牌号,硅,Si,铁,Fe,铜,Cu,锰,Mn,镁,Mg,铬,Cr,锌,Zn,钛,Ti,其他,铝,Al,2A12,LY12,0.5,0.5,3.84.9,0.30.9,1.21.8,0.3,0.15,余量,机械性能（Mechanical properties）分析：,铝合金牌号及状态,抗拉强度,(MPa)Tensile Strength,屈服强度,(MPa)Yield Strength,伸长率,(%)Elongation,布氏硬度,Hardness,2A12,410,265,12,5,2A11,这是应用最早的一种硬铝，一般称为标准硬铝，具有中等强度，在退火、刚淬火和热状态下可塑性尚好，可热处理强化，在淬火和自然时效状态下使用，点焊焊接性良好，用,LY11,作焊料进行气焊及氩弧焊时有裂纹倾向；包铝板材有良好的稳定性，不包铝的则抗蚀性不高，在加热超过,100,有产生晶间腐蚀倾向。表面阳极氧化和涂漆能可靠地保护挤压与锻造零件免于腐蚀。可切削在淬火时效状态下尚好，在退火状态时不良。,化学成分,(Chemical Composition Limits wt%),分析：,合金牌号,旧牌号,硅,Si,铁,Fe,铜,Cu,锰,Mn,镁,Mg,铬,Cr,锌,Zn,钛,Ti,其他,铝,Al,2A11,LY11,0.7,0.7,3.84.8,0.40.8,0.40.8,0.3,0.15,余量,机械性能（Mechanical properties）分析：,铝合金牌号及状态,抗拉强度,(MPa)Tensile Strength,屈服强度,(MPa)Yield Strength,伸长率,(%)Elongation,布氏硬度,Hardness,2A11,370,215,12,6,标准：,GB/T3880-2006,特性及适用范围：,5052,属于,Al-Mg,系合金,使用范围广泛,特别是建筑业离不开此合金，是最有前途的合金。耐蚀性好，焊接性优良，冷加工性较好，并具有中等强度。,5052,的主要合金元素为镁，具有良好的成形加工性能、抗蚀性、焊接性，中等强度，用于制造飞机油箱、油管、以及交通车辆、船舶的钣金件，仪表、街灯支架与铆钉、五金制品、电,-,器外壳等。,AL-Mn,系合金，是应用最广的一种防锈铝，这种合金的强度高，特别是具有抗疲劳强度：塑性与耐腐蚀性高，不能热处理强化，在半冷作硬化时塑性尚好，冷作硬化时塑性低，耐腐蚀好，焊接性良好，可切削性能不良，可抛光。用途主要用于要求高的可塑性和良好的焊接性，在液体或气体介质中工作的低载荷零件，如油箱，汽油或润滑油导管，各种液体容器和其他用深拉制作的小负荷零件：线材用来做铆钉。,化学成分,(Chemical Composition Limits wt%),分析：,合金牌号,旧牌号,硅,Si,铁,Fe,铜,Cu,锰,Mn,镁,Mg,铬,Cr,锌,Zn,钛,Ti,其他,铝,Al,5052,0.25,0.4,0.1,0.1,2.22.8,0.150.35,0.1,余量,机械性能（Mechanical properties）分析：,铝合金牌号及状态,抗拉强度,(MPa)Tensile Strength,屈服强度,(MPa)Yield Strength,伸长率,(%)Elongation,布氏硬度,Hardness,5052,173305,65,7,5754,具有中等强度、良好的耐蚀性、焊接性及易于加工成形等特点，是,Al,Mg,系合金中的典型合金。在国外，不同热处理状态的,5754,是汽车制造业（轿车车门、模具、密封件）、制罐工业所用的主要材料。应用范围：,5754,广泛应用于焊接结构、贮槽、压力容器、船舶结构与海上设施、运输槽罐以及用于要求有优良加工性能、优良耐蚀性、高疲劳强度、高可焊性和中等静态强度的场合。,化学成分,(Chemical Composition Limits wt%),分析：,合金牌号,旧牌号,硅,Si,铁,Fe,铜,Cu,锰,Mn,镁,Mg,铬,Cr,锌,Zn,钛,Ti,其他,铝,Al,5754,0.4,0.4,0.1,0.5,2.63.6,0.3,0.2,0.15,余量,机械性能（Mechanical properties）分析：,铝合金牌号及状态,抗拉强度,(MPa)Tensile Strength,屈服强度,(MPa)Yield Strength,伸长率,(%)Elongation,布氏硬度,Hardness,5754,165265,8,6061,合金的主要合金元素是镁和硅，并形成,Mg2Si,相。若含有一定量的锰和铬，可以中和铁的坏作用；有时还添加少量的铜或锌，以提高合金的强度，而又不使其抗蚀性有明显降低；导电材料中还有少量的铜，以抵消钛及铁对导电性的不良影响；锆或者钛能细化晶粒与控制再结晶组织；为了改善可切削性能，可加入铅与铋。在,Mg2Si,中，,Mg/Si,比为,1.73,，在热处理状态下，,Mg2Si,固熔于铝中，使合金有人工时效硬化功能。,6061-T651,是,6061,合金的主要状态，是经热处理预拉伸工艺生产的高品质铝合金产品，其强度虽不能与,2xxx,系或,7xxx,系相比，但其镁，硅合金特性多，具有加工性能极佳、优良的焊接特点及电镀性、良好的抗腐蚀性、韧性高及加工后不变形、材料致密无缺陷及易于抛光、上色膜容易、氧化效果极佳等优良特点。,代表用途包括航天固定装置、电器固定装置、通讯领域，也广泛应用于自动化机械零件、精密加工、模具制造、电子及精密仪器、,SMT,、,PC,板焊锡载具等等。,A6061-T651,精密加工,/,模具用鋁合金板 产品特点：,1.,良好的可成型性、可焊接性。,2.,强度高。,3.,可使用性好，接口特点优良。,4.,易于加工，容易涂层。,5.,抗腐蚀性、抗氧化性好。主要用途：航空固定装置，卡车，塔式建筑，船，管道及其他需要有强度、可焊性和抗腐蚀性能的建筑上的应用的领域。如：飞机零件、照相机镜头、耦合器、船舶配件和五金、电子配件和接头、装饰用或各种五金、铰链头、磁头、刹车活塞、水利活塞、电器配件、阀门和阀门零件。,化学成分,(ChemicalCompositionLimitswt%),分析：,合金,硅,铁,铜,锰,镁,铬,锌,钛,牌号,Si,Fe,Cu,Mn,Mg,Cr,Zn,Ti,6061,0.4-0.8,0.7,0.15-0.4,0.15,0.8-1.2,0.04-0.35,0.25,0.15,机械性能（Mechanicalproperties）分析：,铝合金牌号及状态,抗拉强度,(MPa)TensileStrength,屈服强度,(MPa)YieldStrength,伸长率,(%)Elongation,布氏硬度,Hardness,6061,290,240,9,90,机械性能分析（TypicalMechanicalProperties）,铝合金牌号及状态,拉伸强度,屈服强度,延伸率,(250MPa),(250MPa),500kg,力,10mm,球,Elongation,ALLOYANDTEMPER,UltimateTensileStrength,UltimateTensileStrength,6061-T651,310,276,12,物理性能分析（TypicalPhysicalProperties）,铝合金牌号及状态,热膨胀系数（,20-100,）,um/m.k,熔点范围（）,电导率,20,（,68F,）（,%ACS,）,ALLOYANDTEMPER,AverageCoefficientOfThermalExpansion,MeltingRange,ElectricalConductivity,6061-T6/6061-T651,23.6,580-650,43,9,国家铝板带标准：,GB/T3880-20065083,是是高镁合金,在不可热处理合金中强度良好，耐蚀性、可切削性良好。阳极化处理后表面美观。电弧焊性能良好。,5083,合金中的主要合金元素为镁，具有良好的抗蚀性与可焊接性能，以及中等强度。优良的抗腐蚀性能使,5083,合金广泛用于海事用途如船舶，以及汽车、飞机焊接件、地铁轻轨，需严格防火的压力容器（如液体罐车、冷藏车、冷藏集装箱）、制冷装置、电视塔、钻探设备、交通运输设备、导弹零件、装甲等。,5083,属于,Al-Mg-Si,系合金,使用范围广泛,特别是建筑业离不开此合金，是最有前途的合金。耐蚀性好，焊接性优良，冷加工性较好，并具有中等强度。,5083,的主要合金元素为镁，具有良好的成形加工性能、抗蚀性、焊接性，中等强度，用于制造飞机油箱、油管、以及交通车辆、船舶的钣金件，仪表、街灯支架与铆钉、五金制品、电器外壳等。,5083,铝板常用于船舶、舰艇、车辆用材、汽车和飞机板焊接件、需严格防火的压力容器、致冷装置、电视塔、钻探设备、交通运输设备、导弹元件、装甲等。,化学成分,(ChemicalCompositionLimitswt%),分析：,合金,硅,铁,铜,锰,镁,铬,锌,钛,牌号,Si,Fe,Cu,Mn,Mg,Cr,Zn,Ti,5083,0.4,0.4,0.1,03.-1.0,4.4-4.9,0.05-0.25,0.25,0.15,铝合金牌号及状态,拉伸强度,屈服强度,硬度,延伸率,(250MPa),(250MPa),500kg,力,10mm,球,1.6mm(1/16in),厚度,Elongation,ALLOYANDTEMPER,UltimateTensileStrength,UltimateTensileStrength,Hardness,5083H112,275-350,210,65,16,物理性能分析（TypicalPhysicalProperties）,铝合金牌号及状态,热膨胀系数（,20-100,）,um/m.k,熔点范围（）,电导率,20,（,68F,）（,%ACS,）,ALLOYANDTEMPER,AverageCoefficientOfThermalExpansion,MeltingRange,ElectricalConductivity,5083H112,23.4,570-640,29,10,7075,精密加工,/,模具用铝合金板,7XXX,系列为铝、锌、镁合金，商用最强力合金之一，普通抗腐蚀性能及机械性能。,7075,属,Al-Zn-Mg-Cu,系超硬铝，,7075,合金是,20,世纪,40,年代末期就已应用于飞机制造业，至今仍在航空工业上得到广泛应用的超高强度变形铝合金。其特点是，固溶处理后塑性好，热处理强化效果特别好，在,150,以下有高的强度，并且有特别好的低温强度；焊接性能差；有应力腐蚀开裂倾向；需经包铝或其他保护处理使用。双级时效可提高合金抗应力腐蚀开裂的能力。在退火和刚淬火状态下的塑性稍低于同样状态的,2A12.,稍优于,7A04,，板材的静疲劳,.,缺口敏感，应力腐蚀性能优于,7A04,，其中以,7075T651,尤为上品，被誉为铝合金中最优良的产品，强度高，远胜于软钢。此合金具有良好的机械性能及阳极反应，是典型的航空用铝。用于制造飞机结构及其他要求强度高、抗蚀性能强的高应力结构件，如飞机上、下翼面壁板，桁条，隔框等。固溶处理后塑性好，热处理强化效果特别好，在,150,以下的有高的强度，并且有特别好的低温强度，焊接性能差,有应力腐蚀开裂倾向,双级时效可提高抗,SCC,性能。,化学成分,(ChemicalCompositionLimitswt%),分析：,合金,硅,铁,铜,锰,镁,铬,锌,钛,牌号,Si,Fe,Cu,Mn,Mg,Cr,Zn,Ti,7075,0.4,0.5,1.2-20,0.3,2.1-2.9,0.18-0.28,5.1-6.1,0.2,机械性能（Mechanicalproperties）分析：,铝合金牌号及状态,抗拉强度,(MPa)TensileStrength,屈服强度,(MPa)YieldStrength,伸长率,(%)Elongation,布氏硬度,Hardness,7075,524,462,11,150,机械性能分析（TypicalMechanicalProperties）,铝合金牌号及状态,拉伸强度,屈服强度,硬度,延伸率,(250MPa),(250MPa),500kg,力,10mm,球,1.6mm(1/16in),厚度,Elongation,ALLOYANDTEMPER,UltimateTensileStrength,UltimateTensileStrength,Hardness,7075-T651,572,503,150,11,物理性能分析（TypicalPhysicalProperties）,铝合金牌号及状态,热膨胀系数（,20-100,）,um/m.k,熔点范围（）,电导率,20,（,68F,）（,%ACS,）,ALLOYANDTEMPER,AverageCoefficientOfThermalExpansion,MeltingRange,ElectricalConductivity,7075-T651,23.6,475-635,33,11,2024,的合金元素为铜，被称为硬铝，具有很高的强度和良好的切削加工性能，但耐腐蚀性较差。广泛应用于飞机结构（蒙皮、骨架、肋梁、隔框等）、铆钉、导弹构件、卡车轮毂、螺旋桨元件及其他各种结构件。,化学成分,(Chemical Composition Limits wt),合金牌号,2024,Cu,Si,Fe,Mn,Mg,Zn,Cr,Ti,Pb.Bi,Al,3.8-4.9,0.5,0.5,0.3-0.9,1.2-1.8,0.25,0.1,0.15,余量,典型合金2024-T351机械和物理性能(Typical Mechanical Properties),焊接性,切削性,耐蚀性,电导率,20(68)(,IACS),密度,(20)(g/cm3),受限,很好,差,30-40,2.78,抗拉强度,(25C MPa),屈服强度,(25C MPa),硬度,500kg,力,10mm,球,延伸率,1.6mm(1/16in),厚度,最大剪应力,Mpa,472,325,120,10,285,12,2017,的合金元素为铜，是第一个获得工业应用的,2,系合金，具有很高的强度和良好的切削加工性能，但耐腐蚀性较差。主要应用于铆钉、通用机械零件、飞机、船舶、交通、建筑结构件、运输工具结构件、螺旋桨元件及配件。为应用最早的一种硬铝,一般称为标准硬铝,具有中等强度,在退火、刚淬火和热状态下可塑性尚好,可热处理强化,在淬火和自然时效状态下使用,点焊焊接性良好，进行气焊及氩弧焊时有裂纹倾向；包铝板材有良好的腐蚀稳定性。可切削在淬火时效状态下尚好，在退火状态时不良。,化学成分,(Chemical Composition Limits wt%),分析：,合金牌号,旧牌号,硅,Si,铁,Fe,铜,Cu,锰,Mn,镁,Mg,铬,Cr,锌,Zn,钛,Ti,其他,铝,Al,2017,0.20.8,0.7,3.54.5,0.41.0,0.40.8,0.1,0.25,0.15,余量,机械性能（Mechanical properties）分析：,铝合金牌号及状态,抗拉强度,(MPa)Tensile Strength,屈服强度,(MPa)Yield Strength,伸长率,(%)Elongation,布氏硬度,Hardness,2017,370,240,8,13,2A14,从成分看即属于硬铝合金又属于锻铝合金,与,2A50,相比，因含铜量较高，故强度较高,热强性较好,但在热态下的塑性不如,2A50,好，合金具有良好的可切削性,接触焊、点焊和滚焊性能良好,电弧焊和气焊性能差；可进行热处理强化,有挤压效应；耐蚀性不高,人工时效时有检间腐蚀倾向。,化学成分,(Chemical Composition Limits wt%),分析：,合金牌号,旧牌号,硅,Si,铁,Fe,铜,Cu,锰,Mn,镁,Mg,铬,Cr,锌,Zn,钛,Ti,其他,铝,Al,2A14,0.61.2,0.7,3.94.8,0.41.0,0.40.8,0.1,0.3,0.15,余量,机械性能（Mechanical properties）分析：,铝合金牌号及状态,抗拉强度,(MPa)Tensile Strength,屈服强度,(MPa)Yield Strength,伸长率,(%)Elongation,布氏硬度,Hardness,2014,440,10,14,标准：,GB/T3190-1996,主要特征及应用范围：为,AL-Mn,系合金，是应用最广的一种防锈铝，这种合金的强度不高（稍高于工业纯铝），不能热处理强化，故采用冷加工方法来提高它的力学性能：在退火状态有很高的塑性，在半冷作硬化时塑性尚好，冷作硬化时塑性低，耐腐蚀好，焊接性良好，可切削性能不良。用途主要用于要求高的可塑性和良好的焊接性，在液体或气体介质中工作的低载荷零件，如油箱，汽油或润滑油导管，各种液体容器和其他用深拉制作的小负荷零件,化学成分,(Chemical Composition Limits wt%),分析：,合金牌号,旧牌号,硅,Si,铁,Fe,铜,Cu,锰,Mn,镁,Mg,铬,Cr,锌,Zn,钛,Ti,其他,铝,Al,3A21,LF21,0.6,0.7,0.2,1.01.6,0.05,0.1,0.15,余量,机械性能（Mechanical properties）分析：,铝合金牌号及状态,抗拉强度,(MPa)Tensile Strength,屈服强度,(MPa)Yield Strength,伸长率,(%)Elongation,布氏硬度,Hardness,3A21,120-160,85,15,3003,为,AL-Mn,系合金，是应用最广的一种防锈铝，这种合金的强度不高（稍高于工业纯铝），不能热处理强化，故采用冷加工方法来提高它的力学性能。用于加工需要有良好的成形性能、高的抗蚀性可焊性好的零件部件，或既要求有这些性能又需要有比,1XXX,系合金强度高的工作，如厨具、食物和化工产品处理与贮存装置，运输液体产品的槽、罐，以薄板加工的各种压力容器与管道一般器物、散热片、化妆板、影印机滚筒、船舶用材。,化学成分,(Chemical Composition Limits wt%),分析：,合金牌号,旧牌号,硅,Si,铁,Fe,铜,Cu,锰,Mn,镁,Mg,铬,Cr,锌,Zn,钛,Ti,其他,铝,Al,3003,0.6,0.7,0.050.2,1.01.5,0.1,余量,机械性能（Mechanical properties）分析：,铝合金牌号及状态,抗拉强度,(MPa)Tensile Strength,屈服强度,(MPa)Yield Strength,伸长率,(%)Elongation,布氏硬度,Hardness,3003,142-178,115,16,3004,系列也属于铝锰合金的一个系列，强度比,3003,高，成形性优良，耐蚀性良好，要求有比,3003,合金更高强度的零部件。主要应用在化工产品生产与储存装置，薄板加工件，建材、建筑挡板，电缆管道，下水道，各种灯具零部件、饮料罐、浪板、建材、彩色铝板、电灯头。易拉罐（,3004,合金）。铝板带国家标准,(GB/T3880-2006),，适用于铝合金板带材料的统一标准。,化学成分,(ChemicalCompositionLimitswt%),分析：,合金牌号,旧牌号,硅,Si,铁,Fe,铜,Cu,锰,Mn,镁,Mg,铬,Cr,锌,Zn,钛,Ti,3004,0.3,0.7,0.25,1.01.5,0.81.3,0.25,机械性能（Mechanicalproperties）分析：,铝合金牌号及状态,抗拉强度,(MPa)TensileStrength,屈服强度,(MPa)YieldStrength,伸长率,(%)Elongation,3004,150285,118,17,（标准,GB/T3190-1996,）,5A02,为,Al-Mg,系防锈铝，与,3A21,相比，,5A02,强度较高特别是具有较高的疲劳强度；塑性与耐蚀性高，在这方面与,3A21,相似；热处理不能强化，用电阻焊和原子氢焊焊接性良好，氩弧焊时有形成结晶裂纹的倾向,;,合金在冷作硬化和半冷作硬化状态下可切削性较好，退火状态下可切削性不良，可抛光。,化学成分,(Chemical Composition Limits wt%),分析：,合金牌号,旧牌号,硅,Si,铁,Fe,铜,Cu,锰,Mn,镁,Mg,铬,Cr,锌,Zn,钛,Ti,其他,铝,Al,5A02,LF2,0.4,0.4,0.1,0.150.4,2.02.8,0.15,余量,机械性能（Mechanical properties）分析：,铝合金牌号及状态,抗拉强度,(MPa)Tensile Strength,屈服强度,(MPa)Yield Strength,伸长率,(%)Elongation,布氏硬度,Hardness,5A02,147,14,18,【,标准：,GB/T 6893-2000】5A03,为,Al-Mg,系防锈铝，合金的性能与,5A02,相似，但因含镁量比,5A02,稍高，且加入少量的硅，故其焊接性比,5A02,好，合金用气焊,.,氩弧焊,.,点焊和滚焊的焊接性能都很好，其他性能两者无大差别。,化学成分,(Chemical Composition Limits wt%),分析：,合金牌号,旧牌号,硅,Si,铁,Fe,铜,Cu,锰,Mn,镁,Mg,铬,Cr,锌,Zn,钛,Ti,其他,铝,Al,5A03,LF3,0.50.8,0.5,0.1,0.30.6,3.23.8,0.2,0.15,余量,机械性能（Mechanical properties）分析：,铝合金牌号及状态,抗拉强度,(MPa)Tensile Strength,屈服强度,(MPa)Yield Strength,伸长率,(%)Elongation,布氏硬度,Hardness,5A03,175,80,15,19,【,标准：,GB/T 6893-2000】5A05,为铝镁系防锈铝（,5B05,的含镁量稍高于,5A05,）,强度与,5A03,相当，热处理不能强化,;,退火状态塑性高，半冷作硬化时塑性中等,;,用氢原子焊、点焊、气焊、氩弧焊时焊接性能尚好,;,抗腐蚀性高,可切削性能在退火状态低劣，半冷作硬化时可切削性尚好，制造铆钉时需进行阳极化处理。,化学成分,(Chemical Composition Limits wt%),分析：,合金牌号,旧牌号,硅,Si,铁,Fe,铜,Cu,锰,Mn,镁,Mg,铬,Cr,锌,Zn,钛,Ti,其他,铝,Al,5A05,LF5,0.5,0.5,0.1,0.30.6,4.85.5,0.2,余量,机械性能（Mechanical properties）分析：,铝合金牌号及状态,抗拉强度,(MPa)Tensile Strength,屈服强度,(MPa)Yield Strength,伸长率,(%)Elongation,布氏硬度,Hardness,5A05,225,110,15,20,【,标准：,GB/T 6892-2000】,5A06,为,Al-Mg,系防锈铝,5A06,铝板具有较高的强度和腐蚀稳定性,在退火和挤压状态下塑性尚好，用氩弧焊的焊缝气密性和焊缝塑性尚可,气焊和点焊其焊接接头强度为基体强度的,90,95%;,可切削性能良好。使用范围广泛,特别是建筑业离不开此合金，是最有前途的合金。耐蚀性好，焊接性优良，冷加工性较好，并具有中等强度。,化学成分,(Chemical Composition Limits wt%),分析：,合金牌号,旧牌号,硅,Si,铁,Fe,铜,Cu,锰,Mn,镁,Mg,铬,Cr,锌,Zn,钛,Ti,其他,铝,Al,5A06,LF6,0.4,0.4,0.1,0.50.8,5.86.8,0.2,0.020.1,余量,机械性能（Mechanical properties）分析：,铝合金牌号及状态,抗拉强度,(MPa)Tensile Strength,屈服强度,(MPa)Yield Strength,伸长率,(%)Elongation,布氏硬度,Hardness,5A06,315,160,15,21,5083,合金中的主要合金元素为镁，具有良好的抗蚀性与可焊接性能，以及中等强度。优良的抗腐蚀性能使,5083,合金广泛用于海事用途如船舶，以及汽车、飞机焊接件、地铁轻轨，需严格防火的压力容器（如液体罐车、冷藏车、冷藏集装箱）、制冷装置、电视塔、钻探设备、交通运输设备、导弹零件、装甲等。,化学成分,(chemical composition limits wt%),合金牌号,硅,Si,铁,Fe,铜,Cu,锰,Mn,镁,Mg,铬,Cr,锌,Zn,钛,Ti,其他,铝,Al,5083,0.4,0.4,0.1,0.41.0,4.04.9,0.050.25,0.25,0.15,余量,典型合金5083-h112机械和物理性能(typical mechanical&physical properties),焊接性,切削性,耐蚀性,电导率,20(68),密度,(%iacs),(20)(g/cm3),很好,一般,很好,30-40,2.8,抗拉强度,(25c mpa),屈服强度,(25c mpa),硬度,500kg,力,10mm,球,延伸率,1.6mm(1/16in),厚度,最大剪应力,mpa,315,230,65,14,180,22,标准：,GB/T 3880.2-2006 5083,是是高镁合金,在不可热处理合金中强度良好，耐蚀性、可切削性良好。阳极化处理后表面美观。电弧焊性能良好。,5083,合金中的主要合金元素为镁，具有良好的抗蚀性与可焊接性能，以及中等强度。优良的抗腐蚀性能使,5083,合金广泛用于海事用途如船舶，以及汽车、飞机焊接件、地铁轻轨，需严格防火的压力容器（如液体罐车、冷藏车、冷藏集装箱）、制冷装置、电视塔、钻探设备、交通运输设备、导弹零件、装甲等。,5083,属于,Al-Mg-Si,系合金,使用范围广泛,特别是建筑业离不开此合金，是最有前途的合金。耐蚀性好，焊接性优良，冷加工性较好，并具有中等强度。,5083,的主要合金元素为镁，具有良好的成形加工性能、抗蚀性、焊接性，中等强度，用于制造飞机油箱、油管、以及交通车辆、船舶的钣金件，仪表、街灯支架与铆钉、五金制品、电器外壳等。,5083,铝板常用于船舶、舰艇、车辆用材、汽车和飞机板焊接件、需严格防火的压力容器、致冷装置、电视塔、钻探设备、交通运输设备、导弹元件、装甲等。,化学成分,(Chemical Composition Limits wt%),分析：,合金,硅,铁,铜,锰,镁,铬,锌,钛,其 他,铝,牌号,Si,Fe,Cu,Mn,Mg,Cr,Zn,Ti,每个,总计,Al,5083,0.4,0.4,0.1,03.-1.0,4.4-4.9,0.05-0.25,0.25,0.15,0.05,0.15,余量,铝合金牌号及状态,拉伸强度,屈服强度,硬度,延伸率,(250MPa),(250MPa),500kg,力,10mm,球,1.6mm(1/16in),厚度,Elongation,ALLOYAND TEMPER,Ultimate Tensile Strength,Ultimate Tensile Strength,Hardness,5083H112,275-350,210,65,16,物理性能分析（Typical Physical Properties）,铝合金牌号及状态,热膨胀系数（,20-100,）,um/m.k,熔点范围（）,电导率,20,（,68F,）（,%ACS,）,电阻率,20,（,68F）m/m,ALLOYAND TEMPER,Average Coefficient OfThermal Expansion,Melting Range,Electrical Conductivity,ElectricalResistivity,5083H112,23.4,570-640,29,0.059,23,6063,主要合金元素为镁与硅，具有加工性能极佳、优良的可焊接性、挤出性及电镀性、良好的抗腐蚀性、韧性，易于抛光、上色膜，阳极氧化效果优良，是典型的挤压合金。,6063,铝合金型材以其良好的塑性、适中的热处理强度、良好的焊接性能以及阳极氧化处理后，表面华丽的色泽等诸多优点而被广泛应用于建筑型材、灌溉管材、供车辆、台架、家具、升降机、栅栏等用的管、棒、型材。,6063,铝合金广泛用于建筑铝门窗、幕墙的框架，为了保证门窗、幕墙具有高的抗风压性能、装配性能、耐蚀性能和装饰性能，对铝合金型材综合性能的要求远远高于工业型材标准。,6063,铝合金 铝板 铝棒的成分、性能与典型用途,6063,合金中的主要合金元素为镁与硅，具有加工性能极佳、优良的可焊接性、挤出性及电镀性、良好的抗腐蚀性、韧性，易于抛光、上色膜，阳极氧化效果优良，是典型的挤压合金。广泛应用于建筑型材、灌溉管材、供车辆、台架、家具、升降机、栅栏等用的管、棒、型材。,化学成分,(chemical composition limits wt%),合金牌号,cu,si,fe,mn,mg,zn,cr,ti,pb.bi,al,6063,0.1,0.20.6,0.35,0.1,0.45 0.9,0.1,0.1,0.1,/,余量,机械性能（Mechanical properties）分析：,铝合金牌号及状态,抗拉强度,(MPa)Tensile Strength,屈服强度,(MPa)Yield Strength,伸长率,(%)Elongation,布氏硬度,Hardness,6063,205,170,9,典型合金6063-t5机械和物理性能(typical mechanical&physical properties),焊接性,切削性,耐蚀性,电导率,密度,20(68)(%iacs),(20)(g/cm3),很好,一般,很好,55-63,2.75,抗拉强度,屈服强度,硬度,延伸率,最大剪应力,(25c mpa),(25c mpa),500kg,力,10mm,球,1.6mm(1/16in),厚度,mpa,185,145,60,12,115,24,7A04,主要特征及应用范围：属,Al-Zn-Mg-Cu,系超高强度铝合金，亦称超硬铝，是超硬铝中相当成熟,.,使用较久和较广的一个合金。强度高，热处理强化效果好，退火和新淬火状态下塑性中等；与硬铝不同，人工时效状态下的耐蚀性比自然时效状态的耐蚀性好，且自然时效进程慢，需经过,3,个月后才能达到时效硬化峰值，故,7A04,在淬火人工时效状态下使用。其缺点是组织稳定性不高，低频疲劳强度低，有应力腐蚀破裂倾向。合金点焊焊接性良好，气焊不良，热处理后可切削性良好，但退火后的可切削性不佳。,化学成分,(ChemicalCompositionLimitswt%),分析：,合金牌号,旧牌号,硅,Si,铁,Fe,铜,Cu,锰,Mn,镁,Mg,铬,Cr,锌,Zn,钛,Ti,7A04,LC4,0.5,0.5,1.42.0,0.20.6,1.82.8,0.10.25,5.07.0,0.1,机械性能（Mechanicalproperties）分析：,铝合金牌号及状态,抗拉强度,(MPa)TensileStrengt