压铸件外观常见的缺陷.ppt

单击此处编辑母版标题样式,单击此处编辑母版文本样式,第二级,第三级,第四级,第五级,*,压铸件外观常见的缺陷,2,成形不良（,non-fills,）,3,崩缺,(damage),4,5,夹层（,laminations,）,6,油污，脏污（,grease,，,dirt,）,7,气孔（,porosity,，,pore,）,8,缩孔（,shrink,）,9,缩凹（,dent,）,10,气泡（,blister,）,11,表面不光滑,12,裂纹（,crack,）,13,粘模（,solder,）,14,扣模，拉伤（,drag,）,15,顶凸（,protruding),16,起皮（,double-skin,）,17,变形（,bending,，,warping,）,18,龟裂，模裂纹（,turtle cracks,network cracks,）,19,多肉（,Excessive material),20,错模、滑块退位,（,mis-match),21,22,披锋，飞边（,flash,）,23,台阶浅旳产品,24,断芯（,core broken,）,25,水口崩缺（,ingate broken,）,26,顶针过高,27,夹渣（,inclusions,）,28,加工后起皮（夹层）,29,黑皮（,unmachined area),30,31,牙平,32,乱牙,33,牙拧不究竟,34,发霉（,oxidation,）,35,加工后有毛刺,36,铝屑,37,加工后螺纹孔残留铝屑,38,刀纹,39,崩刀造成加工不到位,40,夹具压崩产品,41,加工后槽位台阶,42,倒角返工不良,43,无倒角,44,倒角台阶,45,倒角漏加工,46,漏加工,47,48,加工孔变形,49,印痕,50,压痕,51,裂纹,52,碰伤,53,碰伤变形,54,55,通孔不通,56,水口打磨不到位,毛刺清除不洁净,57,产品冲裂,58,孔口处毛刺,59,镶件位毛刺,60,过抛,61,抛丸后钢珠残留,62,水口位下凹,63,严重锉刀痕,64,色差,65,笔迹,66,研磨后石头残留,67,浸渗液残留,